30% Glass fiber Reinforced PBT

Features

The reinforced PBT/PET has high melting point, high deflection temperature and good heat

 stability, high mechanical strength . Low friction coefficient is low so it is abrasion resistant.

 It has very good electrical properties, too. The humidity absorption is low. The mechanical 

properties, electrical properties and dimensional stability are affected barely when 

absorbing moisture to saturate. PBT with excellent chemical resistance is inert to most 

of the chemicals except hot water and alkali. Reinforced PBT/PET is easy to process . 

The surface of its products is smooth and glossy. 

Uses

For thin-walled and complex-shaped products, electric motor components, home appliance 

stents, capacitor shell, load break switch, electronic equipment fan blade, motor shell, Terminal board, relay, automatic 

circuit block device, fuse block, coil skeleton, plug and circuit connector and phone 

distribution box.

Test item

Test condition

Test method

Test result

Unit

Physical propeties

Density

ASTM D792

1.55

g/cm3

Water absorption 

saturation, 23°C 

ASTM D570

0.6

%

Molding shrinkage

ASTM D955

0.3-0.5

%

Glass fiber content

ASTM D2117

30

%

Melting Index

250°C,5KG

ASTM D1238

10

g/10min

Mechanical properties

Tensile strength

23°C,DAM

ASTM D638

120

Mpa

Tensile elongation

23°C,DAM

ASTM D638

30

%

Flexural strength

23°C,DAM

ASTM D790

180

Mpa

Flexural modulus

23°C,DAM

ASTM D790

7800

Mpa

Notched Izod impact(1/8") 

23°C,DAM

ASTM D256

9.5

KJ/m2

Thermal properties

Deflection temperature

1.82Mpa

ASTM D648

215

°C

Melting point

ASTM D2117

—

°C

Flammability

UL 94

HB

—

Machining parameters 

Drying temperature

—

100

°C

Drying time

—

4

hr

Processing temperature

—

235-255

°C

Remarks

30% Glass fiber reinforced