Reinforced PA66 glass filled nylon

Features

PA66's mechanical properties, such as the strength, rigidity, creep resistance, and Izod impact strength is increased due to the fiber skeleton built in the parts. Mineral reinforcement improves the warping of injection molding ,accuracy of dimension and the surface gloss and reduced the molding warping.

Uses

Mechanical parts, electric tools, coil skeleton, auto parts, railway components,

 fuse box, Bearing maintainer and sport equipment.

Test item

Test condition

Test method

Test result

Unit

Physical properties

Density

ASTM D792

1.32

g/cm3

Water absorption 

saturation, 23°C 

ASTM D570

1.7

%

Molding shrinkage

ASTM D955

0.3-0.6

%

Glass fiber content

ASTM D2117

25

%

Melting Index

250°C,5KG

ASTM D1238

7.7

g/10min

Mechanical properties

Tensile strength

23°C,DAM

ASTM D638

142

Mpa

Tensile elongation

23°C,DAM

ASTM D638

5

%

Flexural strength

23°C,DAM

ASTM D790

197

Mpa

Flexural modulus

23°C,DAM

ASTM D790

6500

Mpa

Notched Izod impact(1/8") 

23°C,DAM

ASTM D256

7.8

KJ/m2

Thermal properties

Deflection temperature

0.45Mpa

ASTM D648

245

°C

Melting point

ASTM D2117

250

°C

Flammability

UL 94

HB

—

Machining parameters 

Drying temperature

—

100

°C

Drying time

—

4

hr

Processing temperature

—

245-265

°C

Remarks

25% Glass fiber reinforced